| 规格级别 | 外观颜色 | ||
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTMD1505 | 0.950 | g/cm³ | |
| 物理性能 | 密度 | ISO1183 | 0.950 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 5.5to9.3 | g/10min | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ISO1133 | 5.5to9.3 | g/10min | |
| 物理性能 | 醋酸乙烯含量 | 23.5to26.5 | wt% | ||
| 物理性能 | MaleicAnhydrideContent | 1600 | ppm | ||
| 机械性能 | TensileStrength2(Break,2.80mm,CompressionMolded) | ASTMD638 | 26.0 | MPa | |
| 机械性能 | TensileStress(Break,2.80mm,CompressionMolded) | ISO527-2/5A/50 | 26.0 | MPa | |
| 机械性能 | TensileElongation2(Break,2.80mm,CompressionMolded) | ASTMD638 | 600to900 | % | |
| 机械性能 | TensileStrain(Break,2.80mm,CompressionMolded) | ISO527-2/5A/50 | 600to900 | % | |
| 硬度 | DurometerHardness(ShoreA,2.80mm,CompressionMolded) | ASTMD2240 | 82 | ||
| 硬度 | ShoreHardness(ShoreA,2.80mm,CompressionMolded) | ISO868 | 82 | ||
| 热性能 | 维卡软化温度 | ASTMD15253 | 43.0 | °C | |
| 热性能 | 维卡软化温度 | ISO306/A | 43.0 | °C | |
| 热性能 | 熔融温度 | ISO11357-3 | 80.0 | °C | |
| 热性能 | RingandBallSofteningPoint | ASTME28 | 150 | °C | |