| 规格级别 | 外观颜色 | ||
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTMD1505 | 0.924 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 2.0 | g/10min | |
| 机械性能 | TensileStrength2(Break,0.0318mm) | ASTMD638 | 23.0 | MPa | |
| 薄膜 | FilmThickness-Recommended/Available3 | <1.0mil(25µ) | |||
| 薄膜 | 弹性模量-MD | ASTMD882 | 164 | MPa | |
| 薄膜 | 弹性模量-TD | ASTMD882 | 188 | MPa | |
| 薄膜 | TensileStrength-MD2(Yield,32µm) | ASTMD882 | 10.0 | MPa | |
| 薄膜 | TensileStrength-TD2(Yield,32µm) | ASTMD882 | 9.50 | MPa | |
| 薄膜 | TensileStrength-MD2(Break,32µm) | ASTMD882 | 23.0 | MPa | |
| 薄膜 | TensileStrength-TD2(Break,32µm) | ASTMD882 | 20.0 | MPa | |
| 薄膜 | TensileElongation-MD2(Break,32µm) | ASTMD882 | 230 | % | |
| 薄膜 | TensileElongation-TD2(Break,32µm) | ASTMD882 | 580 | % | |
| 薄膜 | DartDropImpact4(32µm) | ASTMD1709A | 140 | g | |
| 薄膜 | ElmendorfTearStrength-MD2(32µm) | ASTMD1922 | 240 | g | |
| 薄膜 | ElmendorfTearStrength-TD2(32µm) | ASTMD1922 | 140 | g | |
| 热性能 | 熔融温度 | 175to185 | °C | ||
| 光学性能 | Gloss2(45°,31.8µm) | ASTMD2457 | 75 | ||
| 光学性能 | 雾度5 | ASTMD1003 | 6.0 | % | |