| 规格级别 | 刚性，高,高密度,低速凝固晶点,食品接触的合规性,均聚物,可加工性，良好 共挤薄膜,薄膜挤出 | 外观颜色 | |
| 该料用途 | 混合 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 0.960 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 0.38 | g/10min | |
| 薄膜 | 薄膜厚度-经测试 | 38 | µm | ||
| 薄膜 | SecantModulus-1%Secant,MD(38µm,BlownFilm) | ASTMD882 | 830 | MPa | |
| 薄膜 | SecantModulus-1%Secant,TD(38µm,BlownFilm) | ASTMD882 | 1330 | MPa | |
| 薄膜 | TensileStrength-MD(Yield,38µm,BlownFilm) | ASTMD882 | 26.0 | MPa | |
| 薄膜 | TensileStrength-TD(Yield,38µm,BlownFilm) | ASTMD882 | 23.0 | MPa | |
| 薄膜 | TensileStrength-MD(Break,38µm,BlownFilm) | ASTMD882 | 53.0 | MPa | |
| 薄膜 | TensileStrength-TD(Break,38µm,BlownFilm) | ASTMD882 | 23.0 | MPa | |
| 薄膜 | ElmendorfTearStrength-MD(38µm,BlownFilm) | ASTMD1922 | 18 | g | |
| 薄膜 | 埃尔曼多夫抗撕强度-TD(38µm,吹塑薄膜) | ASTMD1922 | 1800 | g | |
| 薄膜 | OxygenTransmissionRate(23°C,0%RH,38µm,BlownFilm) | ASTMD3985 | 1700 | cm³/m²/24hr | |
| 薄膜 | WaterVaporTransmissionRate(38°C,100%RH,38µm,BlownFilm) | ASTMF1249 | 4.2 | g/m²/24hr | |
| 硬度 | 肖氏硬度(邵氏D) | ASTMD2240 | 68 | ||
| 热性能 | 维卡软化温度 | ASTMD1525 | 129 | °C | |
| 光学性能 | Gloss(45°,38.0µm,BlownFilm) | ASTMD2457 | 5 | ||
| 光学性能 | 雾度(38.0µm,吹塑薄膜) | ASTMD1003 | 81 | % | |
| ADDITIONAL INFORMATION | 补充信息 | TestMethod | NominalValue | Unit | |
| ADDITIONAL INFORMATION | LowFrictionPuncture-BlownFilm(38.0µm) | InternalMethod | 300 | J/cm | |
【免责声明】
塑米城发布此信息目的在于方便用户查阅，对于所有的数据及建议等给用户带来的不确定因素和后果概不负责。因此，用户与使用者在使用此产品之前，应向生产商或采购商索取或确认数据的可靠性。