| 规格级别 | 良好的撕裂强度,可加工性，良好,低速凝固晶点,低密度,辛烯共聚单体,抗氧化性,食品接触的合规性,良好的热封性,韧性良好 共挤出成型,薄膜挤出 | 外观颜色 | |
| 该料用途 | 层压板,薄膜 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 0.917 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 1.0 | g/10min | |
| 薄膜 | 薄膜厚度-经测试 | 25 | µm | ||
| 薄膜 | SecantModulus-1%Secant,MD(25µm,BlownFilm) | ASTMD882 | 126 | MPa | |
| 薄膜 | SecantModulus-1%Secant,TD(25µm,BlownFilm) | ASTMD882 | 132 | MPa | |
| 薄膜 | TensileStrength-MD(Yield,25µm,BlownFilm) | ASTMD882 | 9.00 | MPa | |
| 薄膜 | TensileStrength-TD(Yield,25µm,BlownFilm) | ASTMD882 | 9.00 | MPa | |
| 薄膜 | TensileStrength-MD(Break,25µm,BlownFilm) | ASTMD882 | 46.0 | MPa | |
| 薄膜 | TensileStrength-TD(Break,25µm,BlownFilm) | ASTMD882 | 42.0 | MPa | |
| 薄膜 | TensileElongation-MD(Break,25µm,BlownFilm) | ASTMD882 | 540 | % | |
| 薄膜 | TensileElongation-TD(Break,25µm,BlownFilm) | ASTMD882 | 760 | % | |
| 薄膜 | 落锤冲击(25µm,吹塑薄膜) | ASTMD1709A | 400 | g | |
| 薄膜 | ElmendorfTearStrength-MD(25µm,BlownFilm) | ASTMD1922 | 300 | g | |
| 薄膜 | ElmendorfTearStrength-TD(25µm,BlownFilm) | ASTMD1922 | 450 | g | |
| 薄膜 | SealInitiationTemperature(25µm,BlownFilm) | 100 | °C | ||
| 光学性能 | 光泽度 | 45°,25.0µm,BlownFilm2 | ASTMD2457 | 72 | |
| 光学性能 | 光泽度 | 45°,25.0µm,BlownFilm3 | ASTMD2457 | 37 | |
| 光学性能 | 雾度 | 25.0µm,BlownFilm2 | ASTMD1003 | 7.0 | % |
| 光学性能 | 雾度 | 25.0µm,BlownFilm3 | ASTMD1003 | 16 | % |
| ADDITIONAL INFORMATION | 补充信息 | TestMethod | NominalValue | Unit | |
| ADDITIONAL INFORMATION | LowFrictionPuncture-BlownFilm(25.0µm) | InternalMethod | 790 | J/cm | |