| 规格级别 | 良好的强度,良好的热封性,低速凝固晶点,光滑性,低密度,抗氧化性,抗结块性,辛烯共聚单体,韧性良好 薄膜挤出 | 外观颜色 | |
| 该料用途 | 层压板,食品包装,薄膜 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 0.921 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 0.75 | g/10min | |
| 薄膜 | 薄膜厚度-经测试 | 25 | µm | ||
| 薄膜 | SecantModulus-1%Secant,MD(25µm,BlownFilm) | ASTMD882 | 180 | MPa | |
| 薄膜 | SecantModulus-1%Secant,TD(25µm,BlownFilm) | ASTMD882 | 205 | MPa | |
| 薄膜 | TensileStrength-MD(Yield,25µm,BlownFilm) | ASTMD882 | 10.0 | MPa | |
| 薄膜 | TensileStrength-TD(Yield,25µm,BlownFilm) | ASTMD882 | 10.0 | MPa | |
| 薄膜 | TensileStrength-MD(Break,25µm,BlownFilm) | ASTMD882 | 57.0 | MPa | |
| 薄膜 | TensileStrength-TD(Break,25µm,BlownFilm) | ASTMD882 | 46.0 | MPa | |
| 薄膜 | TensileElongation-MD(Break,25µm,BlownFilm) | ASTMD882 | 500 | % | |
| 薄膜 | TensileElongation-TD(Break,25µm,BlownFilm) | ASTMD882 | 800 | % | |
| 薄膜 | 落锤冲击(25µm,吹塑薄膜) | ASTMD1709A | 550 | g | |
| 薄膜 | ElmendorfTearStrength-MD(25µm,BlownFilm) | ASTMD1922 | 370 | g | |
| 薄膜 | ElmendorfTearStrength-TD(25µm,BlownFilm) | ASTMD1922 | 650 | g | |
| 光学性能 | 光泽度(45°,25.0µm,吹塑薄膜) | ASTMD2457 | 58 | ||
| 光学性能 | 雾度(25.0µm,吹塑薄膜) | ASTMD1003 | 10 | % | |
| ADDITIONAL INFORMATION | 补充信息 | TestMethod | NominalValue | Unit | |
| ADDITIONAL INFORMATION | LowFrictionPuncture2(25.0µm) | InternalMethod | 600 | J/cm | |