| 规格级别 | 光学性能,食品接触的合规性,抗穿孔性,低密度,良好的撕裂强度,辛烯共聚单体,低速凝固晶点,抗氧化性 共挤出成型,薄膜挤出 | 外观颜色 | |
| 该料用途 | 流延薄膜,层压板,拉伸缠绕 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 0.917 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 4.0 | g/10min | |
| 薄膜 | 薄膜厚度-经测试 | 20 | µm | ||
| 薄膜 | SecantModulus-1%Secant,MD(20µm,CastFilm) | ASTMD882 | 100 | MPa | |
| 薄膜 | SecantModulus-1%Secant,TD(20µm,CastFilm) | ASTMD882 | 120 | MPa | |
| 薄膜 | TensileStrength-MD(Yield,20µm,CastFilm) | ASTMD882 | 7.50 | MPa | |
| 薄膜 | TensileStrength-TD(Yield,20µm,CastFilm) | ASTMD882 | 7.00 | MPa | |
| 薄膜 | TensileStrength-MD(Break,20µm,CastFilm) | ASTMD882 | 32.0 | MPa | |
| 薄膜 | TensileStrength-TD(Break,20µm,CastFilm) | ASTMD882 | 25.0 | MPa | |
| 薄膜 | TensileElongation-MD(Break,20µm,CastFilm) | ASTMD882 | 470 | % | |
| 薄膜 | TensileElongation-TD(Break,20µm,CastFilm) | ASTMD882 | 780 | % | |
| 薄膜 | ElmendorfTearStrength-MD(20µm,CastFilm) | ASTMD1922 | 380 | g | |
| 薄膜 | ElmendorfTearStrength-TD(20µm,CastFilm) | ASTMD1922 | 540 | g | |
| 光学性能 | 光泽度(45°,20.0µm,铸造薄膜) | ASTMD2457 | 85 | ||
| 光学性能 | 雾度(20.0µm,铸造薄膜) | ASTMD1003 | 0.80 | % | |
| ADDITIONAL INFORMATION | 补充信息 | TestMethod | NominalValue | Unit | |
| ADDITIONAL INFORMATION | LowFrictionPuncture-CastFilm(20.0µm) | InternalMethod | 830 | J/cm | |
| ADDITIONAL INFORMATION | UltimateElongation-CastFilm(20.0µm) | InternalMethod | 360 | % | |